Document Type : Research Paper

Authors

1 University of Tikrit –College of Education

2 University of Tikrit –College of engineering.

Abstract

Polycrystalline samples of high temperature superconductivity of the type 2223, Bi2-xTlxSr2-yBayCa2Cu3O10+ have been prepared by using solid state reaction process. The influence of the substitution of Tl for Bi and Ba for Sr have been studed with different rates (x=0.1-0.4) and (y= 0.1-0.4) at variable sintering temperature, sinterinr time and annealing at 850ºC for 24 h, at average heating 2ºC/min. The best Tc value obtained for the compound is x=0.3,y=0.3 . The x-ray data of all superconductor samples showed a tetragonal structure with a high ratio of Bi-2223 superconducting phase and the resistivity measurements were done using the electrical resistively instruments.The substitution of Tl by Bi and Ba by Sr increases the grain size of the superconductingphase and the density of the pellets. Also give a best value of Tc =133 K respectively

Keywords

Main Subjects

  1. Z. M. Galasiewiez “Superconductivity and Quantum Fluid”, Pergoman Press, Warszawa, (1970).
  2.   M. Valldor, P. Boullay, J. Axn and I. Bryntse, Journal of Solid State Chemistry , V , 153 , p.106, (2000).
  3.  Wang Z.Z., J.G. Clrard, P.Sl. Luo, F. Rullier Al Benque, and H Allon AH, Conference Proceding Vol. 696 (1) PP. L844-898 December 18 (2003).
  4.  Yuan, Y, J. Jiag, X.Y. Gai. Applied Physics Letters Vol. 84(12) PP. 2127-2129 March 22 (2004).
  5. Ali A.D., "study the structure and electrical properties of Bi2Ba2Ca2Cu3O10+d High Temperature Superconductor", Ph.D. Thesis , University of Mosul (2007).
  6. E. Kh. Al-Shakarchi, "The Variation of the Structure and phase Transformation in Y-Ba-Cu-O High Temperature Superconductor Compound with IsovalentSusbstitution" ph.D. Thesis, University of Baghdad, College of Science, (1997).
  7. William D.Callister, JR. Matrials Science And Engineering An Introduction. John Wiley and   Sons, Inc.2000. 53-58,85,839.
  8. C. W. Chu, Phys. Rev. Letters., V.58, p.908, (1987).
    1. K. A. Richardson “The Manufacture of High Temperature Superconducting Tapes and Film”, (1999).

10. S.N. Putilin, E. V. Antupov, O. chmaissemm and M. Marezio, Nnature, V. 362, p.226, (1993).